Alternative compositions of oriented strand boards (OSB) made with commercial woods produced in Brazil

• Autores: Lina Bufalino, Andrea Aparecida Ribeiro Corrêa, Vânia Aparecida de Sá, Lourival Marin Mendes, Natália Amarante Almeida, Vinnicius Dordenoni Pizzol
• Localización: Maderas: Ciencia y tecnología, ISSN 0717-3644, ISSN-e 0718-221X, Vol. 17, Nº. 1, 2015, págs. 105-116
• Idioma: inglés
• Enlaces
  • Texto completo (pdf)
• Resumen

  • This work aimed to investigate the feasibility of using and mixing Toona ciliata, Eucalyptus urophylla/grandis and Pinus oocarpa woods in OSB production. Three one- species and four mixed-species combinations were compared. Layer structure varied by positioning different wood species in the surface and core of the panels. Phenol- formaldehyde (PF) adhesive was applied at 9% for all OSB panels. Three-layer mats with mass proportion of 25/50/25% for surface/core/surface were produced. Pressing time was 8 min, under a 4 MPa pressure and temperature of 180°C. Physical and mechanical properties were evaluated and compared to EN (300) commercialization standard. Most OSB panels did not fully attain such requirements. OSB panels made with Eucalyptus urophylla/grandis and Pinus oocarpa woods have potential to be commercialized as OSB/1 and OSB/2 types, respectively. Among panels made with T. ciliata wood, those produced with this species in the surface and Eucalyptus urophylla/grandis wood in the core met the requirements established for OSB/1 commercialization. Eucalyptus wood has great potential to substitute Pinus wood in OSB production. The utilization of T. ciliata wood for OSB production decreased mechanical performance, but remarkably enhanced water resistance properties.