Compósitos de poliacrilonitrila/fibra de bananeira preparados in situ

  • Autores: Luanda Silva de Moraes, Juliana da Silva, Daniele C. Bastos
  • Localización: Revista Iberoamericana de Polímeros, ISSN 1988-4206, ISSN-e 0121-6651, Vol. 16, Nº. 6, 2015, págs. 273-279
  • Idioma: portugués
  • Enlaces
  • Resumen
    • English

      Natural fibers are now widely applied in polymer composites for its abundance and biodegradability. Polymeric composites prepared in situ polymerization is a way to obtain a material with good dispersion of load in the matrix. In this work, banana fiber was subjected to a chemical treatment that aimed to provide a better interaction of the fiber/matrix. The PAN/fiber composites were synthesized in situ polymerization. The results illustrate that the microscopy of the composite showed good interaction with the polymer. This behavior was confirmed in the test of hardness which has registered a tendency for the mechanical properties with increasing fiber content in the composite.

    • português

      As fibras naturais são atualmente muito aplicadas em compósitos poliméricos devido a sua abundância e biodegradabilidade. Compósitos poliméricos preparados in situé uma forma de obter um material com boa dispersão da carga na matriz. Neste trabalho, a fibra de bananeira foi submetida a um tratamento químico que teve por finalidade propiciar uma melhor interação fibra/matriz. Os compósitos de PAN/fibra foram sintetizados in situ. Os resultados de microscopia ilustraram que a fibra apresentou boa interação com o polímero. Esse comportamento foi confirmado no ensaio de dureza, o qual informou uma tendência de aumento da propriedade mecânica com o aumento do teor de fibra no compósito.


Fundación Dialnet

Dialnet Plus

  • Más información sobre Dialnet Plus

Opciones de compartir

Opciones de entorno