Reemplazo del cuarzo por ceniza de tamo de arroz en la manufactura de gres porcelánico

  • Autores: Jerrison Delgado Trujillo, Juan Pablo Martínez Chica, Álvaro Guzmán Aponte, Silvio Delvasto Arjona, Vicente Amigó Borrás, Enrique Sánchez Vilches
  • Localización: Revista EIA, ISSN-e 1794-1237, Vol. 12, Nº. 23, 2015, págs. 41-50
  • Idioma: español
  • Títulos paralelos:
    • Muda-se o quartzo por cinza de casca de arroz na fabricação de porcelanato
    • Porcelain stoneware tile manufacturing using rice straw ash as quartz replacement
  • Enlaces
  • Resumen
    • español

      En este documento se presentan los resultados de una investigación basada en el uso de un material alternativo como lo es la ceniza de tamo de arroz (CTA), en sustitución del material de relleno (cuarzo) utilizado para la manufactura de gres porcelánico. Para ello, fue preparada una mezcla estándar (RS_0) (15 % cuarzo, 45 % feldespato, 25 % arcilla caolinítica y 15 % caolín), y dos mezclas más donde la CTA sustituyó al cuarzo en porcentajes del 25 % y 50 % (RS_25 y RS_50, respectivamente). Especímenes de las pastas obtenidas fueron moldeados, secados, y cocidos. A partir de los valores de absorción de agua y resistencia a la flexión, los especímenes cocidos de las mezclas estándar (RS_0) y aquellas con adición de CTA RS_25 y RS_50, fueron clasificados como baldosas de gres porcelánico prensadas en seco pertenecientes al grupo BIa, conforme a la normativa ISO 13006 (resistencia a flexión > 35 MPa y absorción de agua ≤ 0,5 %); sin embargo, en aquellos especímenes cocidos RS_50 el intervalo óptimo de cocción más estrecho y el fenómeno de hinchamiento deben ser tenidos en cuenta a la hora de establecer la temperatura óptima de cocción; lo que indica que debe tenerse un mayor control del proceso de cocción de estas mezclas. Los resultados permitieron concluir que la CTA bajo las condiciones de obtención, sí reemplaza parcialmente el material de relleno utilizado en la elaboración de gres porcelánico.

    • English

      In this research are presented the results of using rice straw ash (RSA) as substitute of filler material for manufacturing stoneware tiles. Specimens of standard porcelain stoneware tile (RS_0) were compared to porcelain stoneware tiles where quartz was replaced by RSA in the formulation in percentages of 25% and 50%, respectively (RS_25 and RS_50). Specimens of semidry triaxial mixtures were prepared by uniaxial pressing, followed by drying and sintering. Porcelain stoneware tile specimens RS_0, RS_25 and RS_50 reached bending strength and water absorption values were in accordance with standard ISO 13006 (Annex G, BIa) (≥ 35 MPa and < 0.5%, respectively). However, porcelain stoneware tile specimens RS_50 showed a shorter temperature range for firing than RS_0 and bloating phenomenon must be considered. This indicates that more careful control is required during the firing process of this porcelain. It was concluded that filler material can be substituted positively by RSA in stoneware tile pastes.

    • português

      Neste artigo são apresentados os resultados de uma investigação com base na utilização de um material alternativo, tal como a cinza de casca de arroz (CCA), substituindo o material de enchimento (quartzo) utilizado para a fabricação de porcelanato. Para isso, foi preparada uma mistura padrão (RS_0) (15% de quartzo, feldspatos 45%, 25% de argila caulinítico e 15% de caulino), e duas misturas mais, onde CTA substitui percentagens de quartzo de 25% e 50% (RS_25 e RS_50 respectivamente). Espécimes das massas obtidas foram moldados, secadas e cozidas. A partir dos valores de absorção de água e resistência à flexão, as misturas padrão cozidas (RS_0) e aqueles com adição CTA RS_25 e RS_50, foram classificadas como louças de porcelanato pressionadas em seco que pertence ao grupo Bla, de acordo com a norma ISO 13006 (resistência à flexão> 35 MPa, e a absorção de água ≤ 0,5%); embora, nos espécimes preparados RS_50 o intervalo ideal de cozimento mais estreito e o fenômeno de inchamento devem ser levados em conta quando for estabelecida a temperatura de cozimento ideal; indicando que deve ser maior o controle sobre o processo de cozimento dessas misturas. Os resultados permitiram concluir que o CTA de acordo com as condições de produção, sim substitui parcialmente o material de enchimento usado na fabricação de porcelanato.