Titanium-Zirconium Binary Alloy as Dental Implant Material: Analysis of the Influence of Compositional Change on Mechanical Properties and In Vitro Biologic Response

• Autores: Tsunglin James Lee, Takao Hanawa, Takeshi Ueno, Naoyuki Nomura, Noriyuki Wakabayashi
• Localización: The International Journal of Oral & Maxillofacial Implants, ISSN-e 0882-2786, Vol. 31, Nº. 3, 2016, págs. 547-554
• Idioma: inglés
• Texto completo no disponible (Saber más ...)
• Resumen

  • Purpose: To evaluate the mechanical properties and biologic response of single-phase Ti-Zr alloys cast in higher-purity casting conditions, with comprehensive compositions (from 10 to 90 mol% of Zr).

    Materials and Methods: The mechanical properties and in vitro biologic response with proportional increase of Zr to Ti-Zr alloy composition were assessed. Tensile strength, surface hardness, and Young's modulus were examined. The in vitro cell response of the alloys was also tested with mouse osteoblast cells.

    Results: Analyses of mechanical tests demonstrated improved strength and reduced Young's modulus on this binary alloy system. In vitro cell culture studies with osteogenic MCT3T-E1 cells exhibited the highest attachment rate with the largest and more mature cells on Ti10Zr, instead of commercially pure Ti, whereas a significantly lower cell attachment rate and delayed alkaline phosphatase-specific activity (ALP) differentiation were detected on Ti50Zr.

    Conclusion: The results revealed that the composition did have an impact on the in vitro biologic response. Ti-Zr alloys with 50-50 mol% composition had a decreased biologic response, although the mechanical properties improved. The overall highest strength was Ti with 30 mol% Zr without significant decrease of biologic response.