Efecto de la corrosión por h 2 so 4 en la difusividad térmica de acero api5l-x52

• Autores: Gabriel Peña Rodríguez, Oscar Flores Macías, Carlos Ángeles Chávez, Jose Antonio Calderon Arenas, Rocio Muñoz Hernández
• Localización: Respuestas, ISSN 0122-820X, ISSN-e 2422-5053, Vol. 9, Nº. 1, 2004, págs. 33-38
• Idioma: español
• Enlaces
  • Texto completo (pdf)
• Resumen
  • español

    In this work present a study of the effect of the H2SO4 corrosion to constant pH of 1.4 in the thermal diffusivity of API5L-X52 pipeline steel. The samples were exposed by 3, 6, 9, 12 and 15 days to the corrosive solution, in an atmosphere with relative average humidity of 57.16% and temperature of 23.6°C. The thermal diffusivity measure was carried out using the photoacoustic technique in a heat transmission configuration. Our results show a decrease of the thermal diffusivity ( a ) with the corrosion time, presenting a behavior that is adjusted to a logistical curve of type decreasing with a saturation limit of 52% of a initial value.

  • español

    Este trabajo presenta el efecto de la corrosión por H2SO4 a pH constante de 1.4 en la difusividad térmica de acero API5L-X52. Las muestras se expusieron por 3, 6, 9, 12 y 15 días a la solución corrosiva, en un ambiente con humedad relativa promedio del 57.16% y a una temperatura de 23.6 °C. La medida de la difusividad térmica se realizó usando la técnica fotoacústica en configuración de transmisión de calor. Nuestros resultados muestran una disminución de la difusividad térmica ( a ) con el tiempo de corrosión, presentando un comportamiento que se ajusta a una curva logística del tipo decrecimiento con un límite de saturación del orden del 52% del valor inicial de A.