Resumen de Materiais compósitos a base de PP e Muscovita

Karollyne Gomes Castro Monsores, Silvia Cristina Alves França, Luanda Silva de Moraes, Shirleny Fontes Santos

• English

  Composites based on polypropylene (PP) and muscovite mica in concentrations varying from 0–20% were obtained via extrusion. The muscovite in natura was processed and after characterization by diffraction X–ray and SEM revealed no alterations in the crystalline structure and maintenance of the lamellar structure. The composites of PP/mica showed a reduced melt index and a progressive increase in the value of the density and hardness of the material. In thermal analysis (TG / DSC) there was slight increase in the decomposition temperature of the Polypropylene in the composites containing 10, 15, and 20% mica. The analysis of the mechanical properties by tensile tests revealed slight increase in the Young's Modulus (610 MPa in pure PP to 750 Mpa in PP/20%mica) attributed to restricted mobility of the polymer chains imposed by the presence of mica.

• português

  Compósitos com base em polipropileno (PP) e mica do tipo muscovita em concentrações variando de 0–20% foram obtidos via extrusão. A muscovita in natura foi beneficiada e caracterizada por difração de raios–X e MEV que revelaram a ausência de alterações na estrutura cristalina e manutenção da estrutura lamelar. Os compósitos de PP/mica obtidos apresentaram redução no índice de fluidez e um aumento progressivo no valor da densidade e na dureza do material. Nas análises térmicas (TG/DSC) verificou–se ligeiro aumento da temperatura de decomposição deslocamento do PP para os compósitos com 10, 15 e 20% de mica. A análise das propriedades mecânicas por meio de ensaios de tração, revelou ligeiro aumento no módulo de Young, (de 610 Mpa no PP puro para 750 Mpa no PP/20%mica) atribuído à restrição da mobilidade das cadeias imposta pela presença da mica.