Effect of oxygen vacancy in tungsten oxide on the photocatalytic activity for decomposition of organic materials in the gas phase

• Autores: Daisuke Fukushi, Akito Sasaki, Hideaki Hirabayashi, Masaaki Kitano
• Localización: Microelectronics reliability, ISSN 0026-2714, Nº. 79, 2017, págs. 1-4
• Idioma: inglés
• Texto completo no disponible (Saber más ...)
• Resumen

  • Abstract The relationship between the oxygen vacancy of tungsten oxide and its ability to decompose organic materials under visible-light irradiation was investigated experimentally. In the field of rechargeable batteries, the highest charge-discharge rate is obtained when tungsten oxide is used as a negative electrode with an O/W ratio of 2.72. This result suggested that the number of oxygen vacancies in tungsten oxide affects the photocatalytic decomposition behavior of organic materials. Therefore, with the aim of increasing the photocatalytic activity of tungsten oxide to decompose organic materials, we attempted to clarify the role of the oxygen vacancy. WO3 − x nanoparticles, including WO2.83 and WO2.72 nanoparticles, were fabricated by changing the annealing temperature in a 10% H2, 90% N2 atmosphere to generate different densities of oxygen vacancies. Tungsten oxide with O/W ratios of 2.83 and 2.72 exhibited no photocatalytic activity for the photodecomposition of organic materials. The maximum decomposition rate was obtained for stoichiometric WO3 (O/W = 3). The reason for the decrease or disappearance of the photodecomposition ability should originate in the increase in the number of electrons generated by the oxygen vacancies. These excess electrons promote the recombination reaction between electrons and holes in WO3 − x, and hence reduce the lifetime of electron-hole pairs.