Thermomechanical properties of compositions based on polysilicates modified with boron cluster anions or SiO2 nanoparticles

• Autores: Elena Malinina, Vera Skachkova, Liudmila Boeva, Andrei Grachev, Galina Lyubimova, Varvara Avdeeva, Irina Kozerozhets, Aleksandr Shaulov, Aleksandr Berlin, Nikolay Kuznetsov
• Localización: Boletín de la Sociedad Española de Cerámica y Vidrio, ISSN 0366-3175, Vol. 59, Nº. 5, 2020, págs. 201-208
• Idioma: español
• Títulos paralelos:
  • Propiedades termomecánicas de composiciones basadas en polisilicatos modificados con aniones de grupos de boro o nanopartículas de SiO2
• Enlaces
  • Texto completo
• Resumen
  • español

    Sodium liquid glass silicate compositions modified with boron cluster anions [B10Cl10]2− or [B10H10]2− or SiO2 nanoparticles have been studied. It is shown that in the silicate matrix, the presence of the polyhedral anions results in nanoscale supramolecular structures formed due to their interaction with silanol groups of silicates. In the range of 20–600°C, the TMA method is used to study the formation of supramolecular associates, as well as the deformation stability of the modified silicate matrix and the softening temperature of the modified polysilicates formed upon thermal exposure.

  • English

    Se han estudiado composiciones de silicato de vidrio líquido de sodio modificadas con aniones poliédricos [B10Cl10]2− o [B10H10]2− o nanopartículas de SiO2. Se muestra que en la matriz de silicato, la presencia de los aniones poliédricos da como resultado estructuras supramoleculares a nanoescala formadas debido a su interacción con grupos de silicatos de silanol. En el rango de 20–600°C, TMA se ha utilizado para estudiar la formación de asociados supramoleculares, así como la estabilidad a la deformación de la matriz de silicato modificado y la temperatura de reblandecimiento de los polisilicatos modificados formados tras la exposición térmica.