• Marulanda Arévalo, José Luddey ; Pérez-Muñoz, Diego ^[1] ; Remolina Millan, Aduljay ^[2]
  1. [1] Universidad Tecnológica de Pereira

     Universidad Tecnológica de Pereira

     Colombia

     
  2. [2] Universidad Pontificia Bolivariana

     Universidad Pontificia Bolivariana

     Colombia

     
• Localización: Revista ION: Investigación, Optimización y Nuevos Procesos en Ingeniería, ISSN-e 2145-8480, ISSN 0120-100X, Vol. 30, Nº. 1, 2017 (Ejemplar dedicado a: Revista ION), págs. 21-31
• Idioma: español
• Títulos paralelos:
  • Resistência à corrosão em um ambiente salino aço carbono revestido com alumínio por aspersão térmica e pintura poli aspártica
  • Corrosion resistance in saline environment of a carbon steel coated with aluminum by thermal spray and painting poly aspartic
• Enlaces
  • Texto completo
• Resumen
  • español

    Se evaluó la resistencia a la corrosión en ambiente salino del acero 1020 recubierto con aluminio por medio de rociado térmico por arco eléctrico y después se aplicó una pintura poliaspártica. Se observó que este sistema presenta una protección en estos ambientes, reduciendo la velocidad de corrosión, en comparación con un sistema de pintura bicapa, el cual consistía en una capa rica en zinc y otra capa de pintura poliaspártica. Se realizó la caracterización del recubrimiento por medio de Microscopia Electrónica de Barrido (MEB) para analizar su comportamiento con respecto al sustrato y a la pintura para conocer variaciones en propiedades como adherencia, topografía y homogeneidad. Se observó que las probetas recubiertas con aluminio por rociado térmico presentan una mayor resistencia a la corrosión en cámara salina que las probetas que no fueron recubiertas y solo estaban protegidas por el sistema bicapa de pintura, aunque la pintura sin rociado térmico tuvo un buen desempeño ya que no falló durante el tiempo estipulado para en ensayo en cámara de niebla salina.

  • English

    The corrosion resistance was assessed in saline environment on a 1020 steel coated with aluminum by arc thermal spraying and then a polyaspartic paint was applied. It was observed that this system has a protection in these environments, reducing the corrosion rate, compared to a bilayer paint system, which consisted of zinc-rich paint layer and polyaspartic coating. Coating characterization was performed by SEM to analyze their behavior with respect to the substrate and paint to meet variations in properties such as adhesion, homogeneity and topography. It was observed that the samples coated with aluminum by thermal spraying showed good corrosion resistance in salt spray the specimens that were not coated, just were protected by the bilayer coating system, even the paint without thermal spraying performed well and that did not fail during the time stipulated in test for salt spray.

  • português

    A resistência à corrosão em solução salina ambiente 1020 aço revestido com alumínio por aspersão térmica de arco foi avaliado e, em seguida, foi aplicada uma tinta poli aspártico. Observou-se que este sistema tem uma protecção nestes ambientes, reduzindo a taxa de corrosão, em comparação com um sistema de pintura de duas camadas, que consistia de um fardo rico em zinco, e outra camada de tinta poliaspártica. Revestimento caracterização foi realizada por SEM para analisar o seu comportamento em relação ao substrato e a tinta para satisfazer as variações nas propriedades de adesão, tais como, a uniformidade e a topografia. Observou-se que as amostras revestidas com alumínio por aspersão térmica apresentam uma maior resistência à corrosão em sal pulverizar as amostras que não foram revestidas sozinho foram protegidas pelo sistema de revestimento de duas camadas, embora bem a tinta sem pulverização térmica e realizada ele não falhou durante o tempo estipulado para ser testado em névoa salina.