Revestimientos compuestos poliméricos con grafeno y óxido de grafeno para la construcción civil - Una revisión

• Lage Souza, Rithyeli ^[1] ; Martins Coura, Igor ^[1] ; Nicodemos Silva, Sidney ^[1]
  1. [1] Centro Federal de Educação Tecnológica de Minas Gerais. Brazil.
• Localización: Revista de Ciencia y Tecnología: RECyT, ISSN 0329-8922, ISSN-e 1851-7587, Vol. 37, Nº. 1, 2022, págs. 45-55
• Idioma: español
• Títulos paralelos:
  • O uso de grafeno e óxido de grafeno em revestimentos de materiais compósitos poliméricos - Uma revisão
  • Polymeric composite coatings with graphene and graphene oxide for the civil construction – A review
• Enlaces
  • Texto completo (pdf)
• Resumen
  • español

    El acero es uno de los materiales más utilizados en la construcción civil y, aunque presenta un comportamiento muy satisfactorio en cuanto a propiedades mecánicas, tiene el inconveniente de ser susceptible a los mecanismos triboquímicos. La corrosión del acero de las estructuras de hormigón armado (Norma NBR 7480 - CA50) puede afectar su integridad estructural, disminuyendo su resistencia a tensiones externas, afectando la vida útil y, por tanto, la durabilidad de la estructura. Las manifestaciones patológicas más comunes en las estructuras de acero son causadas principalmente por la acumulación de humedad, el drenaje deficiente del agua de lluvia y la falta de protección contra el proceso de corrosión. Los recubrimientos poliméricos con grafeno y óxido de grafeno (GO) pueden verse como una solución a estos problemas de corrosión en el acero al carbono debido a su estabilidad química combinada con sus altas propiedades como el grado de hidrofobicidad, impermeabilidad a muchos tipos de sales y gases, en Además de su buena conductividad, las adiciones GO permiten obtener un recubrimiento con mayor durabilidad. Este trabajo tiene como objetivo discutir la influencia de GO en la mejora de los recubrimientos anticorrosión en acero al carbono.

  • English

    Steel is one of the most used materials in civil construction and, although it exhibits a very satisfactory performance in terms of mechanical properties, it has the disadvantage of susceptibility to tribochemical mechanisms. Corrosion of steel of reinforced concrete structures (Standard NBR 7480 - CA50) can affect its structural integrity, decreasing its resistance to external stresses, affecting the service life and, therefore, the durability of the structure. The most common pathological manifestations in steel structures are mainly caused by the accumulation of moisture, deficient drainage of rainwater, and lack of protection against the corrosion process. Polymeric coatings with Graphene and Graphene oxide (GO) can be seen as a solution to these corrosion problems in carbon steel due to its chemical stability combined with its high properties such as the degree of hydrophobicity, impermeability to many types of salts and gases, in addition to its good conductivity, GO additions allow to obtain a coating with greater durability.

  • português

    O aço é um dos materiais mais utilizados na construção civil e, embora apresente um desempenho bastante satisfatório em termos de propriedades mecânicas, apresenta como desvantagem a susceptibilidade a mecanismos triboquímicos. A corrosão do aço destinado ao reforço de estruturas de concreto armado pode afetar sua integridade estrutural, diminuindo sua resistência às tensões externas, afetando a vida útil e, portanto, a durabilidade da estrutura. As manifestações patológicas mais comuns em estruturas de aço são causadas principalmente pelo acúmulo de umidade, drenagem deficiente da água da chuva e falta de proteção contra o processo de corrosão. O óxido de grafeno (GO) pode ser visto como uma solução para esses problemas de corrosão do aço carbono devido a sua estabilidade química aliada a suas altas propriedades como grau de hidrofobicidade, impermeabilidade a diversos tipos de sais e gases, além de boa condutividade, permitem obter um revestimento com maior durabilidade. Neste artigo, foi realizada uma revisão bibliográfica sobre a utilização do óxido de grafeno aplicado ao aço carbono na construção civil, seus principais métodos de processamento de compósitos de matriz polimérica reforçada com óxido de grafeno, bem como verificar se há melhora no as principais propriedades desse material.