Synthesis and characterization of manganese- cobalt solid solutions prepared at low temperature

• EDMUNDO RIOS ^[1] ; PATRICIO LARA ^[1] ; DANIEL SERAFINI ^[1] ; AMBROSIO RESTOVIC ^[2] ; JUAN LUIS GAUTIER ^[1]
  1. [1] Universidad de Santiago de Chile

     Universidad de Santiago de Chile

     Santiago, Chile

     
  2. [2] Universidad de Antofagasta

     Universidad de Antofagasta

     Antofagasta, Chile

     
• Localización: Journal of the Chilean Chemical Society (Boletín de la Sociedad Chilena de Química), ISSN-e 0717-6309, ISSN 0366-1644, Vol. 55, Nº. 2, 2010, págs. 261-265
• Idioma: inglés
• Enlaces
  • Texto completo
• Resumen

  • Two extreme compositions of the manganese-cobalt oxide system Mn xCo3xO4 namely Co3O4 (x = 0) and MnCo2O4 (x = 1) were prepared in powder form at low temperature by thermal decomposition of nitrates in air. The synthesis was conducted at 150°C. The oxides obtained were characterized by different techniques such as X-ray diffraction (XRD), scanning electron microscopy (SEM), surface area determination using the Brunauer-Emmett-Teller (BET) method, thermogravimetric analyses (TGA) and oxidation power (OP). XRD analysis revveals that the oxides crystalhze in a cubic spinel-type structure with a unit cell parameter (a o) that increases as cobalt is replaced by manganese. The MnCo2O4 showed 70 m² g-1 and 13 nm of specific surface area and crystallite size respectively. The crystallite was bigger (20nm) when cobalt-manganese oxide is prepared as athin film. Both compounds exhibited nanometric size. The cationic distributions proposed for both oxides on the basis of the physicochemical characterization results showed an excellent agreement with those obtained from the XRD data refinement performed using the Rietveld method.